1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Η πρόσφυση της ζώνης ανθεκτικής σε υψηλή θερμοκρασία από βαμβακερό καμβά είναι σχετικά χαμηλή και η πρόσφυση της ζώνης ανθεκτικής σε υψηλή θερμοκρασία EP είναι σχετικά υψηλή. η διάρκεια ζωής της ζώνης ανθεκτικής σε υψηλές θερμοκρασίες EP είναι προφανώς μεγαλύτερη από αυτή της ζώνης από βαμβακερό καμβά ανθεκτικό σε υψηλή θερμοκρασία.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Αυτή είναι μια άλλη μέθοδος κόλλησης, αυτή η μέθοδος είναι επίσης δυνατή, αλλά εάν χρησιμοποιείτε αυτήν τη μέθοδο, δώστε προσοχή στα ακόλουθα σημεία:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Συνήθως, όταν η θερμοκρασία βουλκανισμού είναι υψηλότερη από την κρίσιμη θερμοκρασία βουλκανισμού του επιταχυντή και του παράγοντα βουλκανισμού και δεν μπορεί να φτάσει στην κανονική θερμοκρασία βουλκανισμού, η μέθοδος παράτασης του χρόνου βουλκανισμού μπορεί να υιοθετηθεί για να πληροί τις απαιτήσεις ο βουλκανισμός του καουτσούκ. Γενικά, κάθε φορά που η θερμοκρασία είναι χαμηλότερη από 10 βαθμούς, ο χρόνος βουλκανισμού παρατείνεται κατά 2-4 φορές. Φυσικά, για λόγους απόδοσης, δεν συνιστούμε τη χρήση βουλκανισμού χαμηλής-θερμοκρασίας και μακράς διάρκειας.
5. Can core rubbers from different manufacturers be mixed?
Δεν συνιστάται η ανάμειξη καουτσούκ πυρήνα από διαφορετικούς κατασκευαστές, επειδή η φόρμουλα του καουτσούκ πυρήνα από διαφορετικούς κατασκευαστές είναι διαφορετική. Υπάρχουν πολλά είδη σύνθετων παραγόντων στο καουτσούκ, και μερικά από αυτά έχουν αλληλεπιδραστικές αντιδράσεις. Στον τύπο του ίδιου κατασκευαστή, δεν θα υπάρχουν σύνθετοι παράγοντες με δυσμενείς αλληλεπιδραστικές αντιδράσεις, αλλά οι τύποι διαφορετικών κατασκευαστών είναι πολύ διαφορετικοί. Όταν χρησιμοποιείται, μπορεί να υπάρχουν αλληλεπιδραστικές αντανακλάσεις παραγόντων σύνθεσης, οι οποίες θα επηρεάσουν το αποτέλεσμα χρήσης του καουτσούκ πυρήνα.